Ionizing Radiation Sensing with Functionalized and Copper-Coated SWCNT/PMMA Thin Film Nanocomposites.

This paper studies the ionizing radiation effects on functionalized single-walled carbon nanotube (SWCNT)/poly(methyl methacrylate) (PMMA) thin-film nanocomposites [SWNT/PMMA]. The functionalized thin-film devices are made of ferrocene-doped SWCNTs, SWCNTs functionalized with carboxylic acid (COOH), and SWCNTs coated/ modified with copper. The nanocomposite was synthesized by the solution blending method and the resulting nanocomposite was spin-cast on interdigitated electrodes (IDEs). A 160 kV X-ray source was used to irradiate the thin film and changes in the electrical resistance of the nanocomposites due to X-rays were measured using a semiconductor device analyzer. Carboxylic acid functionalized and copper-coated SWCNT/PMMA nanocomposite showed a reduced response to X-rays compared to unfunctionalized SWCNT/PMMA nanocomposite. Ferrocene-doped SWCNT showed a higher sensitivity to X-rays at lower dose rates. This is in contrast to a previous study that showed that similar nanocomposites using functionalized multi-walled CNTs (MWCNTs) had demonstrated an improved response to X-rays ionizing radiation compared to unfunctionalized MWCNTs for all dose rates. Electrical measurements were also performed using the Arduino Nano microcontroller. The result showed that a relatively economical, lightweight-designed prototype radiation sensor based on SWCNT/PMMA thin-film devices could be produced by interfacing the devices with a modest microcontroller. This work also shows that by encapsulating the SWCNT/PMMA thin-film device in a plastic container, the effect of ambient humidity can be reduced and the device can still be used to detect X-ray radiation. This study further shows that the sensitivity of SWCNT to X-rays was dependent on both the functionalization of the SWCNT and the dose rate.