Electrospun Materials Based on Cellulose Acetate Loaded with Rosmarinic Acid with Antioxidant and Antifungal Properties.

Fibrous cellulose acetate (CA) materials loaded with rosmarinic acid (RA) were successfully created by one-pot electrospinning. In order to improve the water solubility of the polyphenolic acid and to facilitate its release from the fibrous materials, the non-ionic water-soluble polyethylene glycol (PEG) was added. Detailed characterization of the fabricated fibrous CA/RA and CA/PEG/RA materials was performed using scanning electron microscopy (SEM), X-ray diffraction analysis (XRD), UV-Vis spectroscopy and water contact angle analysis. The optimal ratio between CA, RA and PEG for preparation of defect-free and uniform fibers was accomplished by varying their concentrations. Furthermore, the incorporation of the PEG improved the hydrophilicity and wettability of the fibrous CA materials. Moreover, PEG facilitated the RA release and over 360 min, the amount released from fibrous CA/PEG/RA fibers was 91%, while that released from CA/RA materials was 53%. Both of the RA-containing fibrous materials, with and without PEG, manifested high antioxidant activity as determined by the DPPH free radical-scavenging method. In addition, the electrospun CA/PEG/RA materials displayed good antifungal activity against