Formation of the Cu+Nb Interlayer in the Inconel 718/Ti6Al4V Multi-Material Obtained by Selective Laser Melting.
Article in Materials (Basel, Switzerland), 2024. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 1 paper.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
1 citing paper in PubMed.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
3 authors.
Funding
Abstract
This study examines the Inconel 718/Ti6Al4V multi-material with a Cu and Nb interlayer produced by SLM. To achieve this, it is necessary to investigate the microstructure, the chemical and phase composition, and the hardness of the interfacial zone in the multi-material samples. Furthermore, it is necessary to determine the impact of interlayer utilization on the mechanical properties of multi-material samples. The investigation showed that the formation of island macro-segregation was observed in all interfacial zones of the multi-material samples. The interfacial zones, Ti6Al4V/Nb and Cu/Inconel 718, exhibited a relatively sharp transition in the chemical composition. In contrast, the Cu/Nb interfacial zone exhibited a gradual transition. The results of the chemical composition study indicated that the width of the Nb/Cu transition zone was approximately 700 μm. No new phases were identified in the production of the multi-material samples. The typical phases were present in the alloy zone, as well as in the Nb/Cu interfacial zone. During the transition from the Ti6Al4V zone to the Inconel 718 zone through the Nb and Cu zones, the average microhardness values changed as follows: 270 → 190 → 120 → 300 HV. The ultimate tensile strength values for the multi-material samples reached 910 MPa.