A Multifunctional Cationic Waterborne Polyurethane System with High Fire-Safety and Antibacterial Performance Enabled by Phosphorous Acid-Protonated Chitosan.

Waterborne polyurethane (WPU) is widely used in flexible films and textile finishing, but its intrinsic flammability, severe melt dripping, and sensitivity to polar additives restrict its fire-safe applications. Herein, a phosphorous acid-protonated chitosan (PCS) was designed as an emulsion-adaptable bio-based modifier and incorporated into cationic WPU via a facile aqueous blending route, yielding transparent multifunctional composite films and flame-retardant textile coatings. Unlike conventional flame-retardant WPU systems that rely on reactive monomers or suffer from poor emulsion compatibility, this work proposes an emulsion-compatible strategy based on PCS, enabling the simultaneous integration of dispersion stability, flame retardancy, and antibacterial functionality within a single system. PCS could be stably accommodated in the WPU latex without visible precipitation or demulsification after centrifugation, and the resulting films preserved a continuous matrix structure with uniformly distributed PCS-rich nanodomains. Rheological analyses revealed that the polar groups of PCS established strong intermolecular associations with urethane segments, strengthening the physical network. The char residue at 700 °C increased from 0.7 wt% for neat WPU to 32.7 wt% for WPU/PCS-5. Meanwhile, WPU/PCS-5 achieved a limiting oxygen index of 35.4% and a UL-94 V-0 rating, while its peak heat release rate and total heat release were reduced by 73.4% and 41.8%, respectively. The composite films also showed nearly complete antibacterial efficiency against